1. Effects of protective colloid on the melamine formaldehyde resin micro - encapsulation
   保護(hù)膠體對(duì)三聚氰胺甲醛樹脂微膠囊成囊性影響的研究
2. Influences of content of soft monomer and hard monomer , emulsifiers , initiators , self - crosslinkable monomer and protective colloid on the properties of emulsion are studied
   研究軟硬單體含量、乳化劑、引發(fā)劑、自交聯(lián)單體、保護(hù)膠體等對(duì)聚合物乳液性能的影響。
3. Self - crosslinkable latex at room temperature with high elasticity is prepared when n - hydroxymethyl acrylamide is used as self - crosslinkable monomer , and poly solidum maleate is applied as protective colloid , and pre - emulsified and semi - continuous seeded emulsion polymerization is adopted
   采用n -羥甲基丙烯酯胺為自交聯(lián)單體，聚馬來(lái)酸鈉為保護(hù)膠體，采用預(yù)乳化半連續(xù)種子乳液聚合工藝，制備出高彈性室溫自交聯(lián)乳液。
4. Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 % , and amount of methyl methacrylate is 40 % , and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1 , and amount of initiator is 0 . 6 % , and amount of self - crosslinkable monomer and protective colloid is 2 % and 0 . 4 % respectively
   研究結(jié)果表明：當(dāng)丙烯酸丁酯的質(zhì)量為60 % ，甲基丙烯酸甲酯的質(zhì)量為40 % ，非離子乳化劑和陰離子乳化劑的質(zhì)量配比為3 : 1 ，引發(fā)劑的質(zhì)量為0 . 6 % ，自交聯(lián)單體的質(zhì)量為2 % ，保護(hù)膠體的質(zhì)量為0 . 4 %時(shí)，可以制備出高彈性自交聯(lián)乳液。